Figure 3. Evolution of the coercive field, measured at room temperature, as a function of the current density after: (o) 1 min and (_) 10 min of annealing time. Reprinted with permission from [21], N. Murillo and J. González, J. Magn. Magn. Mater. 218, 53 (2000). © 2000, Elsevier Science.

Figure 4. Dependence of the coercive force, Hc, with the average grain diameter, D, for the two studied compositions (Fe73^Si13^B9Cu1Nb3 and Fe73 5Si13 5B9CujTa3). Reprinted with permission from [21], N. Murillo and J. González, J. Magn. Magn. Mater. 218, 53 (2000). © 2000, Elsevier Science.